Title ESR, PL and TL studies of LiAlO(2): Mn/Ce phosphor
 
Creator DHABEKAR, B
RAJA, EA
MENON, S
RAO, TKG
KHER, RK
BHATT, BC
 
Subject lithium aluminate
lialo(2)
phosphor
tl
esr
defect centres
f(+)
o(-)
combustion synthesis
pl
mn emission
 
Description LiAlO(2): Mn/Ce phosphor was prepared by combustion synthesis. LiAlO(2): Mn exhibits two thermoluminescence (TL) peaks around 150 and 320 degrees C while LiAlO(2): Cc exhibits TL peaks around 170 and 280 degrees C. PL emission of LiAlO(2): Mn consists of a peak around 500 rim when excited with 450 nm while LiAlO(2): Ce shows a broad band around 400 rim when excited by 320 nm. The TL emission Spectrum of LiAlO(2): Mn consists of a broad hand at 500 run attributed to the (4)T(1) to (6)A(1) transitions or Mn(2+) ion, indicating that Mn2+ is the luminescence centre in LiAlO(2): Mn. ESR studies were carried out to identify defect centres responsible for TL peaks observed in LiAlO(2): Ce. Room temperature ESR Spectrum of irradiated LiAlO(2): Cc phosphor appears to be superposition of at least four distinct centres. Two defect centres (centres I and II) are identified in irradiated LiAlO(2): Cc phosphor and these centres are assigned to O(-) and F(+) centres, respectively. O(-) centre appears to correlate with the 170 degrees C TL peak and F(+) centre appears to correlate with both 170 and 280 degrees C TL peaks in LiAlO(2): Cc. (C) 2007 Elsevier Ltd. All rights reserved.
 
Publisher PERGAMON-ELSEVIER SCIENCE LTD
 
Date 2011-10-22T08:16:16Z
2011-12-15T09:10:49Z
2011-10-22T08:16:16Z
2011-12-15T09:10:49Z
2008
 
Type Article; Proceedings Paper
 
Identifier RADIATION MEASUREMENTS,43,291-294
1350-4487
http://dx.doi.org/10.1016/j.radmeas.2007.11.054
http://dspace.library.iitb.ac.in/xmlui/handle/10054/14849
http://hdl.handle.net/100/1678
 
Source 15th International Conference on Solid State Dosimetry,Delft, NETHERLANDS,JUL 08-13, 2007
 
Language English