Title A study of superplasticity in a Zr-2.5wt%Nb pressure tube alloy
 
Creator SINGH, RN
KISHORE, R
SINHA, TK
KASHYAP, BP
 
Subject behavior
pressure tube
pressurized heavy water reactor
microstructure
transverse
texture
 
Description Zirconium-2.5wt%Nb alloy, used as a pressure tube material of Pressurized Heavy Water Reactors, possess fine microstructure of elongated alpha-Zr grains with a grain-boundary network of beta-Zr and a strong basal pole texture along the transverse (circumferrential) direction of the tube. Transversely oriented flat tensile specimens, machined from a commercial pressure tube were tested at 650-800 degrees by both monotonic and strain-rate cycling (2.68 x 10(-5) - 5.3 x 10(-3) s(-1)) tests in order to study the elevated temperature deformation of this material. It was observed that the alloy exhibited superplasticity in this temperature range, showing high ductility (elongation upto 900 pet.) and strain-rate sensitivity (m similar to 0.3-0.85). Microstructural studies of the deformed structure indicated the transformation of the starting alpha-beta lamellar structure into a fine equiaxed grain-structure and the measured activation energies were found to be 123 kJ/mole at the higher end and 211 kJ/mole at the lower end of the test temperatures. Based on these results it appears that the superplastic behavior is controlled by grain-boundary sliding phenomenon accompanied by niobium diffusion along alpha-beta boundaries at the lower end and lattice diffusion of beta-zirconium at the higher end of the temperature range used in this investigation.
 
Publisher TRANSTEC PUBLICATIONS LTD
 
Date 2011-10-24T05:41:18Z
2011-12-15T09:11:30Z
2011-10-24T05:41:18Z
2011-12-15T09:11:30Z
1997
 
Type Article; Proceedings Paper
 
Identifier SUPERPLASTICITY IN ADVANCED MATERIALS - ICSAM-97,243-,499-504
0-87849-759-5
0255-5476
http://dspace.library.iitb.ac.in/xmlui/handle/10054/15340
http://hdl.handle.net/100/2107
 
Source 1997 International Conference on Superplasticity in Advanced Materials (ICSAM-97),BANGALORE, INDIA,JAN 29-31, 1997
 
Language English