Hydrogen embrittlement behavior of three high manganese stainless steels

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title Hydrogen embrittlement behavior of three high manganese stainless steels
 
Creator RAJA, VS
DEVASENAPATHI, A
 
Description Hydrogen embrittlement (HE) behavior of three commercial grade high Mn stainless steels with varying Ni content was examined. Both constant load tests, under continuous cathodic charging, and constant extension tests of charged samples were carried out. Both the types of tests indicated that the susceptibility of the alloys towards HE to follow the order Grade 3 > Grade 2 > Grade 1 > AISI 304. Cathodic hydrogen charging was found result in the appearance of epsilon(H) martensite in all the three Mn stainless steels, while the tensile test specimen fractured in air was found to contain stress induced alpha' martensite. Since the susceptibility of the alloy towards HE did not seem to correlate with H content of the alloy, the formation of epsilon(H) and alpha' martensites were suggested to be responsible for the higher susceptibility of Mn stainless steels towards HE.
 
Publisher ELSEVIER SCIENCE BV
 
Date 2011-10-27T10:59:29Z
2011-12-15T09:12:34Z
2011-10-27T10:59:29Z
2011-12-15T09:12:34Z
1998
 
Type Proceedings Paper
 
Identifier CORROSION AND ITS CONTROLS, VOLS I AND II,1074-1081
0-444-82916-4
http://dspace.library.iitb.ac.in/xmlui/handle/10054/16274
http://hdl.handle.net/100/2753
 
Source International Conference on Corrosion (CORCON 97),MUMBAI, INDIA,DEC 03-06, 1997
 
Language English