Influence of crystallographic texture on X-ray residual stress measurement for Ti-3wt% Al-2 Vwt% tube material

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title Influence of crystallographic texture on X-ray residual stress measurement for Ti-3wt% Al-2 Vwt% tube material
 
Creator KAPOOR, K
LAHIRI, D
RAO, SVR
SANYAL, T
KASHYAP, BP
 
Subject rod texture
zircaloy-2
metals
x-ray residual stress
texture
ti-3al-2v
elastic constants
 
Description Some inaccuracies are possible during the near-surface residual stress measurement of textured material by X-ray diffraction using the standard multiexposure technique. Diffraction intensities depend on factors like inclination of the sample, the rotation of the beam, and the position of detectors. Low intensity due to texture can result in increased percentage error observed stress values. Anisotropy of elastic constants in textured materials can further increase the errors in measured stress. In the present study, the effect of texture on residual stress has been studied for seamless Ti-3wt%Al-2Vwt% tubes, in pilgered and annealed conditions, by superimposing the residual stress measurements on the pole figure obtained by texture measurement. A general approach has been developed for accurate determination of the stress tensor in textured material. This consists of the selection of inclinations giving rise to high intensity peak, the selection of rotation angles symmetric to the pole figure to get similar intensity from both the detectors (where this is not possible one detector with low intensity is shut off), and the calculation of the bulk X-ray elastic constants using the single crystal elastic data and texture. Cold worked Ti-3wt%Al-2Vwt% tubes had the highest stress along the rolling direction and that is compressive in nature. The principal residual stresses in the pilgered tubes were along the rolling and transverse directions, and annealing leads to reduction and reorientation of the stresses.
 
Publisher AMER SOC TESTING MATERIALS
 
Date 2011-07-17T08:30:58Z
2011-12-26T12:50:12Z
2011-12-27T05:36:20Z
2011-07-17T08:30:58Z
2011-12-26T12:50:12Z
2011-12-27T05:36:20Z
2003
 
Type Article
 
Identifier JOURNAL OF TESTING AND EVALUATION, 31(6), 465-471
0090-3973
http://dspace.library.iitb.ac.in/xmlui/handle/10054/4673
http://hdl.handle.net/10054/4673
 
Language en