ON THE MECHANISM OF THE OXIDATION OF NICRAL-BASE ALLOYS IN AIR AND AIR CONTAINING SULFUR-DIOXIDE

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title ON THE MECHANISM OF THE OXIDATION OF NICRAL-BASE ALLOYS IN AIR AND AIR CONTAINING SULFUR-DIOXIDE
 
Creator KHANNA, AS
QUADAKKERS, WJ
YANG, X
SCHUSTER, H
 
Subject grain-size
resistance
corrosion
behavior
single crystal
superalloy
oxidation
microstructure
grain size
cast and forged alloys
 
Description Oxidation studies have been carried out on NiCrAl-base alloys in air and air containing 1% sulphur dioxide at 1000-degrees-C. The alloys used were in the cast, forged and single-crystalline form. There was considerable difference in the oxidation behavior of the as-cast alloy and that of forged alloy, when the environment contained sulphur dioxide. In the absence of the latter, the behavior of the two alloys was not very different. The oxidation behavior of the single crystals was also very similar to that of the cast and forged alloys, when the atmosphere was oxidizing. A few single-crystalline alloys, however, underwent catastrophic oxidation when about 1% sulphur dioxide gas was present, in a manner similar to that of the cast alloy. Oxidation tests at 1000-degrees-C as well as detailed scale analysis indicated that the different microstructure, especially large difference in grain size was probably the main reason for the large difference in their oxidation behavior.
 
Publisher PLENUM PUBL CORP
 
Date 2011-08-27T06:02:08Z
2011-12-26T12:57:46Z
2011-12-27T05:45:06Z
2011-08-27T06:02:08Z
2011-12-26T12:57:46Z
2011-12-27T05:45:06Z
1993
 
Type Article
 
Identifier OXIDATION OF METALS, 40(3-4), 275-294
0030-770X
http://dx.doi.org/10.1007/BF00664494
http://dspace.library.iitb.ac.in/xmlui/handle/10054/11563
http://hdl.handle.net/10054/11563
 
Language en