Record Details

Effect of tensile deformation on micromagnetic parameters in 0.2% carbon steel and 2.25Cr-1Mo steel

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title Effect of tensile deformation on micromagnetic parameters in 0.2% carbon steel and 2.25Cr-1Mo steel
 
Creator MOORTHY, V
VAIDYANATHAN, S
JAYAKUMAR, T
RAJ, B
KASHYAP, BP
 
Subject barkhausen emission
nondestructive evaluation
stress
magnetization
noise
iron
 
Description The influence of prior tensile deformation on the magnetic Barkhausen emission (MBE) and the hysteresis (B-H) curve has been studied in 0.2% carbon steel and 2.25Cr-1Mo steel under different tempered conditions. This study shows that the micromagnetic parameters can be used to identify the four stages of deformation, namely (i) perfectly elastic, (ii) microplastic yielding, (iii) macroyielding and (iv) progressive plastic deformation. However, it is observed that the MBE profile shows more distinct changes at different stages of tensile deformation than the hysteresis curve. It has been established that the beginning of microplastic yielding and macroyielding can be identified from the MBE profile which is not possible from the stress-strain plot. The onset of microplastic yielding can be identified from the decrease in the MBE peak height. The macroyielding can be identified from the merging of the initially present two-peak MBE profile into a single central peak with relatively higher peak height and narrow profile width. The difference between the Variation of MBE and hysteresis curve parameters with strain beyond macroyielding indicates the difference in the deformation state of the surface and bulk of the sample. (C) 1999 Acta Metallurgica Inc. . .
 
Publisher PERGAMON-ELSEVIER SCIENCE LTD
 
Date 2011-08-24T04:57:28Z
2011-12-26T12:56:45Z
2011-12-27T05:45:56Z
2011-08-24T04:57:28Z
2011-12-26T12:56:45Z
2011-12-27T05:45:56Z
1999
 
Type Article
 
Identifier ACTA MATERIALIA, 47(6), 1869-1878
1359-6454
http://dx.doi.org/10.1016/S1359-6454(99)00048-8
http://dspace.library.iitb.ac.in/xmlui/handle/10054/10764
http://hdl.handle.net/10054/10764
 
Language en