Title Effect of heavy ion irradiation on self-supported diamond sheets
 
Creator PALNITKAR, UMESH
SHIRODKAR, VS
SINGH, MANOJ K
TITUS, E
TYAGI, PK
UNNI, KN
MISRA, DS
AYYUB, PUSHAN
AVASTHI, DK
 
Subject phase transitions
pressure effects
raman spectroscopy
x-ray diffraction
 
Description The self-supported diamond sheets were deposited at various deposition pressure (Pd) using HFCVD technique. The sheets were characterized using X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM). XRD shows the growth of cubic diamond. This is confirmed by Raman spectroscopy showing a sharp line at 1332 cm−1 in all the sheets. The sheets deposited at low pressures show clean sharp facets. The sheets were irradiated with high energy Au and Ag ions of varying energy and dose. The energy range was 100–120 MeV and the dose varied between 1×1012 and 3×1013 ions. Raman spectra showed the reduction in the intensity of diamond line (1332 cm−1) as well as non-diamond band at 1550 cm−1 after irradiation. SEM images of irradiated sheets show a phase transformation on the surface of the crystal. A photoluminescence (PL) signal is observed after the irradiation of the sheets at 2.634 eV.
 
Publisher Elsevier
 
Date 2009-04-28T05:25:15Z
2011-12-08T06:39:29Z
2011-12-26T13:01:43Z
2011-12-27T05:46:24Z
2009-04-28T05:25:15Z
2011-12-08T06:39:29Z
2011-12-26T13:01:43Z
2011-12-27T05:46:24Z
2003
 
Type Article
 
Identifier Diamond and Related Materials 12(10-11), 1771-1775
0925-9635
10.1016/S0925-9635(03)00287-5
http://hdl.handle.net/10054/1259
http://dspace.library.iitb.ac.in/xmlui/handle/10054/1259
 
Language en