Polymer matrix woven fabric composites subjected to low velocity impact: Part I - Damage initiation studies

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title Polymer matrix woven fabric composites subjected to low velocity impact: Part I - Damage initiation studies
 
Creator NAIK, NK
SEKHER, YC
MEDURI, S
 
Subject laminated composites
carbon-fiber
transverse impact
failure behavior
induced fracture
plates subject
cross-ply
delamination
resistance
energy
impact behavior of composites
low velocity impact
damage initiation
woven fabric composites
plain weave fabric
weave geometry
3d finite element analysis
inplane failure function
interlaminar failure function
 
Description An investigation was undertaken to study the damage initiation behavior in polymer matrix laminated composite plates subjected to a transverse central low velocity point impact load. Inplane failure of the layers in the form of matrix cracking/lamina splitting and delaminations were the primary objectives of the study. The study has been carried out using modified Hertz contact law and an inhouse three-dimensional transient finite element analysis (FEA) code. The inplane failure functions and the interlaminar failure functions have been predicted using quadratic failure criteria. The inhouse FEA code was validated with other analytical studies and the experimental results in our earlier work. The present studies have been carried out on different plain weave fabric laminated composite plates, simply supported on ail four sides. For comparison, impact behavior of balanced symmetric crossply (CP) Laminates made of unidirectional (UD) layers and UD composites has been included. The studies have been carried out with plate dimensions of 150 mm x 150 mm with different prate thicknesses. Incident impact velocity in the range of 1 m/sec to 3 m/sec and impactor mass of 50 gm are considered. General observations on the distribution of failure functions and the initiation of damage are presented.
 
Publisher TECHNOMIC PUBL CO INC
 
Date 2011-08-31T10:00:47Z
2011-12-26T12:59:30Z
2011-12-27T05:51:43Z
2011-08-31T10:00:47Z
2011-12-26T12:59:30Z
2011-12-27T05:51:43Z
2000
 
Type Article
 
Identifier JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 19(12), 912-954
0731-6844
http://dx.doi.org/10.1106/X80M-4UEF-CPPK-M15E
http://dspace.library.iitb.ac.in/xmlui/handle/10054/12679
http://hdl.handle.net/10054/12679
 
Language en