Nanocrystalline titanium powders by high energy attrition milling
DSpace at IIT Bombay
View Archive InfoField | Value | |
Title |
Nanocrystalline titanium powders by high energy attrition milling
|
|
Creator |
DABHADE, VV
MOHAN, TRR RAMAKRISHNAN, P |
|
Subject |
nanocrystalline
powders titanium attrition milling |
|
Description |
The present investigation deals with the synthesis of nanocrystalline titanium powders by the high energy attrition milling of micron sized titanium powder in an inert atmosphere. Titanium powders of about 12 pm particle size were subjected to high energy attrition milling in an argon atmosphere. Selecting suitable milling parameters, nanosize (< 100 nm) titanium powders were obtained after 15 h of milling. An average particle size of 35 nm was obtained at 30 It of milling after which the particle size stabilized with continuation of milling to 75 h. The powders after milling for various durations were characterized by XRD, SEM, TEM, ICP-AES and DTA and these results are reported and discussed. (c) 2006
|
|
Publisher |
ELSEVIER SCIENCE SA
|
|
Date |
2011-07-28T14:00:26Z
2011-12-26T12:59:36Z 2011-12-27T05:52:06Z 2011-07-28T14:00:26Z 2011-12-26T12:59:36Z 2011-12-27T05:52:06Z 2007 |
|
Type |
Article
|
|
Identifier |
POWDER TECHNOLOGY, 171(3), 177-183
0032-5910 http://dx.doi.org/10.1016/j.powtec.2006.10.007 http://dspace.library.iitb.ac.in/xmlui/handle/10054/7420 http://hdl.handle.net/10054/7420 |
|
Language |
en
|
|