Title |
High strain rate behavior of woven fabric composites under compressive loading
|
|
Creator |
NAIK, NK
KAVALA, VENKATESWARA RAO |
|
Subject |
compressive strength
epoxy resins strain rate fabrics |
|
Description |
Investigations on high strain rate behavior of composites under compressive loading are presented. Compressive split Hopkinson pressure bar (SHPB) apparatus was used for the studies. Compressive properties of typical plain weave E-glass/epoxy and plain weave carbon/epoxy were evaluated along all the principal directions in the strain rate range of 680ā2890 sā1. It is generally observed that the compressive strength is enhanced at high strain rate loading compared with that at quasi-static loading. During SHPB testing of the specimens, it was observed that the peak force obtained from the strain gage mounted on the transmitter bar is lower than the peak force obtained from the strain gage mounted on the incident bar. The explanation for this is provided based on stress wave attenuation studies.
|
|
Publisher |
Elsevier
|
|
Date |
2009-02-26T10:45:15Z
2011-11-25T17:56:03Z 2011-12-26T13:06:25Z 2011-12-27T05:54:15Z 2009-02-26T10:45:15Z 2011-11-25T17:56:03Z 2011-12-26T13:06:25Z 2011-12-27T05:54:15Z 2008 |
|
Type |
Article
|
|
Identifier |
Materials Science and Engineering: A 474(1-2), 301-311
0921-5093 http://dx.doi.org/10.1016/j.msea.2007.05.032 http://hdl.handle.net/10054/789 http://dspace.library.iitb.ac.in/xmlui/handle/10054/789 |
|
Language |
en
|
|