Effect of chromium nitride coating on the corrosion and wear resistance of stainless steel
DSpace at IIT Bombay
View Archive InfoField | Value | |
Title |
Effect of chromium nitride coating on the corrosion and wear resistance of stainless steel
|
|
Creator |
JAGIELSKI, JACEK
KHANNA, AS KUCINSKI, JACEK MISHRA, DS RACOLTA, P SIOSHANSI, PIRAN TOBIN, ERIC THERESKA, J UGLOV, VLADIMIR VILAITHONG, T VIVIENTE, J SI-ZE YANG ZALAR, ANTON |
|
Subject |
chromium compound
x-ray diffraction wear resistance composition effects |
|
Description |
Ion beam-assisted deposition (IBAD) technique has been used to deposit chromium nitride on the stainless steel substrates. Characterization and performance of this coating was carried out by a round-robin test at various laboratories. About 300 samples, prepared at Spire, USA, were distributed to 10 different laboratories. Characterization of coated materials, carried out using Rutherford backscattering (RBS), X-ray diffraction (XRD), glancing X-ray diffraction, Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS), confirmed a well-adherent layer of chromium nitride with composition and thickness of Cr0.8N0.2 and 1.2 μm, respectively. The performance of the coating was tested by tribological tests: dynamic micro-indentation, micro-hardness, wear and friction, and corrosion tests. The coating was found to be hard with good wear resistance and had enhanced resistance to corrosion in acid media.
|
|
Publisher |
Elsevier
|
|
Date |
2009-03-23T05:11:42Z
2011-11-25T20:03:55Z 2011-12-26T13:07:41Z 2011-12-27T05:55:43Z 2009-03-23T05:11:42Z 2011-11-25T20:03:55Z 2011-12-26T13:07:41Z 2011-12-27T05:55:43Z 2000 |
|
Type |
Article
|
|
Identifier |
Applied Surface Science 156(1-4), 47-64
0169-4332 http://dx.doi.org/10.1016/S0169-4332(99)00350-5 http://hdl.handle.net/10054/1055 http://dspace.library.iitb.ac.in/xmlui/handle/10054/1055 |
|
Language |
en
|
|