Fabrication and Properties of High Performance PEEK/Si(3)N(4) Nanocomposites
DSpace at IIT Bombay
View Archive InfoField | Value | |
Title |
Fabrication and Properties of High Performance PEEK/Si(3)N(4) Nanocomposites
|
|
Creator |
BALAJI, V
TIWARI, AN GOYAL, RK |
|
Subject |
POLY(ETHER ETHER KETONE)
TRIBOLOGICAL BEHAVIOR WEAR BEHAVIOR SLIDING FRICTION COMPOSITES PEEK PARTICLES CARBON POLYETHERETHERKETONE FIBER nanocomposites crystallinity hardness wear rate PEEK |
|
Description |
The crystallization, morphology, micro-hardness, scratch hardness, dynamic modulus, and wear behavior of high performance poly(ether-ether-ketone) (PEEK) matrix nanocomposites reinforced with 0 to 30 wt % silicon nitride (Si(3)N(4)) nanoparticles were reported. The crystallinity of PEEK nanocomposites increases at 2.5 wt % Si(3)N(4) but, thereafter it decreases with increasing Si(3)N(4) content due to the hindrance to the ordering of PEEK chains. The crystallization peak temperature and crystallization onset temperature increases by 14 degrees C for 10 wt % nanocomposite. The melting temperature does not vary significantly with Si(3)N(4) content. SEM shows almost uniform distribution of Si3N4 in the PEEK matrix. The Vickers micro-hardness and scratch hardness increases significantly up to 10 wt % Si(3)N(4) content. The dynamic modulus of nanocomposites increases below and above T(g) of PEEK. The specific wear rate of nanocomposites with 2.5 wt % Si(3)N(4) is reduced significantly and it is lowest at 10 wt % Si(3)N(4). However, the coefficient of friction of nanocomposites is more than that of pure PEEK. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 119: 311-318, 2011
|
|
Publisher |
WILEY-BLACKWELL
|
|
Date |
2012-06-26T03:39:59Z
2012-06-26T03:39:59Z 2011 |
|
Type |
Article
|
|
Identifier |
JOURNAL OF APPLIED POLYMER SCIENCE,119(1)311-318
0021-8995 http://dx.doi.org/10.1002/app.32750 http://dspace.library.iitb.ac.in/jspui/handle/100/13885 |
|
Language |
English
|
|