Enhanced flux pinning in pulsed laser deposited YBa(2)Cu(3)O(7-delta):BaTiO(3) nanocomposite thin films
DSpace at IIT Bombay
View Archive InfoField | Value | |
Title |
Enhanced flux pinning in pulsed laser deposited YBa(2)Cu(3)O(7-delta):BaTiO(3) nanocomposite thin films
|
|
Creator |
JHA, AK
KHARE, N PINTO, R |
|
Subject |
SUPERCONDUCTORS
TEMPERATURE YBCO Nanocomposite Critical currents Vortex pinning |
|
Description |
The effect of incorporation of BaTiO(3)(BTO) nanoparticles on the flux pinning properties of pulsed laser deposited YBCO:BTO thin films was studied. Substantial increase in the critical current density (J(C)) and the pinning force density (F(p)) of the nanocomposite thin films was observed. At 77 K, and zero applied magnetic field, the value of J(C) for YBCO and YBCO:BTO (2%) thin films were 2.93 MA/cm(2) and 6.43 MA/cm(2), respectively. At the same temperature and an applied magnetic field of 4 T, the value of J(C) increases from 3.6 x 10(4) A/cm(2) for YBCO thin film to 2.7 x 10(5) A/cm(2) for YBCO:BTO (2%) nanocomposite thin film. The study of temperature and field dependence of J(C) of YBCO and YBCO:BTO thin films indicates similar type of pinning. The lattice mismatch between YBCO and BTO seems to introduce more defects resulting in the improvement of flux pinning properties. (C) 2011 Elsevier Ltd. All rights reserved.
|
|
Publisher |
PERGAMON-ELSEVIER SCIENCE LTD
|
|
Date |
2012-06-26T08:34:09Z
2012-06-26T08:34:09Z 2011 |
|
Type |
Article
|
|
Identifier |
SOLID STATE COMMUNICATIONS,151(20)1447-1451
0038-1098 http://dx.doi.org/10.1016/j.ssc.2011.07.004 http://dspace.library.iitb.ac.in/jspui/handle/100/14193 |
|
Language |
English
|
|