Improved multiferroic properties in Sm-doped BiFeO3 thin films deposited using chemical solution deposition method
DSpace at IIT Bombay
View Archive InfoField | Value | |
Title |
Improved multiferroic properties in Sm-doped BiFeO3 thin films deposited using chemical solution deposition method
|
|
Creator |
SINGH, SK
TOMY, CV ERA, T ITOH, M ISHIWARA, H |
|
Subject |
FERROELECTRIC PROPERTIES
|
|
Description |
Sm-substituted (0% to 10%) BiFeO3 thin films were fabricated by chemical solution deposition on Ptai/SiO2/Si substrates. X-ray diffraction analysis revealed that no secondary phase appeared even if Bi atoms were substituted with Sm atoms up to 10 at. %. 7.5 at. % Sm-substituted films show improved electrical properties and substitution was effective in improving the coercive field in the films. Sm-substitution shows improved ferroelectric as well as magnetic properties of the films. There is a noticeable reduction in the leakage current density (10(-4) A/cm(2)) and increase in the polarization (70 mu C/cm(2)) when the Sm concentration is kept around 7.5%. The magnetic moment obtained from the saturated magnetization curves shows a value of 0.3 mu(B)/Fe compared to 0.04 mu(B)/Fe for the parent compound. The results are important since it increases the potential of the material as a multiferroic compound. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4714650]
|
|
Publisher |
AMER INST PHYSICS
|
|
Date |
2014-10-14T17:52:50Z
2014-10-14T17:52:50Z 2012 |
|
Type |
Article; Proceedings Paper
|
|
Identifier |
JOURNAL OF APPLIED PHYSICS, 111(10)
http://dx.doi.org/10.1063/1.4714650 http://dspace.library.iitb.ac.in/jspui/handle/100/14616 |
|
Language |
en
|
|