In-situ phase transformation studies of Ni48Mn39In13 melt-spun ribbons
DSpace at IIT Bombay
View Archive InfoField | Value | |
Title |
In-situ phase transformation studies of Ni48Mn39In13 melt-spun ribbons
|
|
Creator |
KUMAR, DMR
RAO, DVS RAO, NVR RAJA, MM SINGH, RK SURESH, KG |
|
Subject |
Magnetic intermetallics
Rapid solidification processing Microstructure Electron microscopy transmission SHAPE-MEMORY ALLOYS MARTENSITIC TRANSFORMATIONS HEUSLER ALLOYS GA ALLOYS TEMPERATURES |
|
Description |
The phase transformation in Ni48Mn39In13 melt-spun ribbons has been studied by employing in-situ transmission electron microscopy (TEM) techniques. At room temperature, the investigations showed the martensite phase consisting of plates with internal stacking faults. This phase exhibited the presence of 7M and 5M modulations. In addition, a small volume fraction of the austenite phase was observed. Upon in-situ heating from room temperature to 95 degrees C, the martensite phase transformed to austenite phase. However, in the subsequent cooling-heating cycles, the martensite phase was retained at high temperature. We discuss our experimental observations and the possible mechanisms for the stabilization of the martensite phase due to thermal cycling. (c) 2012 Elsevier Ltd. All rights reserved.
|
|
Publisher |
ELSEVIER SCI LTD
|
|
Date |
2014-10-16T05:49:37Z
2014-10-16T05:49:37Z 2012 |
|
Type |
Article
|
|
Identifier |
INTERMETALLICS, 25126-130
http://dx.doi.org/10.1016/j.intermet.2012.01.029 http://dspace.library.iitb.ac.in/jspui/handle/100/15379 |
|
Language |
en
|
|