The stress-corrosion cracking susceptibility of near-alpha titanium alloy IMI 834 in presence of hot salt
DSpace at IIT Bombay
View Archive Info| Field | Value | |
| Title |
The stress-corrosion cracking susceptibility of near-alpha titanium alloy IMI 834 in presence of hot salt
|
|
| Creator |
PUSTODE, MD
RAJA, VS PAULOSE, N |
|
| Subject |
Titanium
SEM Stress corrosion MECHANISM MODEL |
|
| Description |
The hot salt stress corrosion cracking (HSSCC) behaviour of a near alpha titanium alloy, IMI 834, was studied using slow strain rate test method in the temperature range 250-450 degrees C. The alloy was found to be susceptible to HSSCC at 300 degrees C and above; and the susceptibility increased with an increase in the test temperature. The secondary cracks grew exponentially with temperature. HSSC cracks initiated at alpha/beta interfaces and grew across the primary alpha grain and along the alpha/beta interfaces. (C) 2014 Elsevier Ltd. All rights reserved.
|
|
| Publisher |
PERGAMON-ELSEVIER SCIENCE LTD
|
|
| Date |
2014-12-28T17:36:57Z
2014-12-28T17:36:57Z 2014 |
|
| Type |
Article
|
|
| Identifier |
CORROSION SCIENCE, 82191-196
0010-938X 1879-0496 http://dx.doi.org/10.1016/j.corsci.2014.01.013 http://dspace.library.iitb.ac.in/jspui/handle/100/17006 |
|
| Language |
English
|
|