High thermoelectric performance of (AgCrSe2)(0.5)(CuCrSe2)(0.5) nano-composites having all-scale natural hierarchical architectures

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title High thermoelectric performance of (AgCrSe2)(0.5)(CuCrSe2)(0.5) nano-composites having all-scale natural hierarchical architectures
 
Creator BHATTACHARYA, S
BOHRA, A
BASU, R
BHATT, R
AHMAD, S
MESHRAM, KN
DEBNATH, AK
SINGH, A
SARKAR, SK
NAVNEETHAN, M
HAYAKAWA, Y
ASWAL, DK
GUPTA, SK
 
Subject THERMAL-CONDUCTIVITY
BULK THERMOELECTRICS
PANOSCOPIC APPROACH
AGCRSE2
NANOSTRUCTURES
POWER
 
Description Recent studies have shown that thermoelectric materials exhibit a high figure-of-merit if it consists of hierarchically organized microstructures that significantly lower the lattice thermal conductivity without any appreciable change in the power factor. Here, we report a new class of thermoelectric (AgCrSe2)(0.5)(CuCrSe2)(0.5) nano-composites synthesized via the vacuum hot pressing of a mixture of the constituents, which naturally consists of phonon scattering centers in a multiscale hierarchical fashion, i.e. atomic scale disorder, nanoscale amorphous structure, natural grain boundaries due to layered structure and mesoscale grain boundaries/interfaces. The presence of a natural hierarchical architecture of different length scales in the composite samples is confirmed by scanning electron and transmission electron microscopy. Detailed characterization reveals that in the composite samples there is a slight migration of Cu into the Ag site. Composite samples exhibit extremely low thermal conductivity similar to 2 mW cm(-1) K-1 at 773 K, which is nearly one third of the pure AgCrSe2 and CuCrSe2. The composite samples exhibit a high ZT similar to 1.4 at 773 K, which is attributed to the scattering of heat carrying phonons of all wavelengths via the natural hierarchical architecture of the material. The ease of synthesis of such high performance (AgCrSe2)(0.5)(CuCrSe2)(0.5) nanocomposites with a natural hierarchical architecture offers a promise for replacing conventional tellurides.
 
Publisher ROYAL SOC CHEMISTRY
 
Date 2014-12-29T04:45:27Z
2014-12-29T04:45:27Z
2014
 
Type Article
 
Identifier JOURNAL OF MATERIALS CHEMISTRY A, 2(40)17122-17129
2050-7488
2050-7496
http://dx.doi.org/10.1039/c4ta04056b
http://dspace.library.iitb.ac.in/jspui/handle/100/17110
 
Language English