Nanocrystalline zinc ferrite films studied by magneto-optical spectroscopy

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title Nanocrystalline zinc ferrite films studied by magneto-optical spectroscopy
 
Creator LISKOVA-JAKUBISOVA, E
VISNOVSKY, S
SIROKY, P
HRABOVSKY, D
PISTORA, J
SAHOO, SC
PRASAD, S
VENKATARAMANI, N
BOHRA, M
KRISHNAN, R
 
Subject THIN-FILMS
TEMPERATURE MAGNETIZATION
ZNFE2O4
SPINELS
GARNETS
 
Description Ferrimagnetic Zn-ferrite (ZnFe2O4) films can be grown with the ferromagnetic resonance linewidth of 40 Oe at 9.5 GHz without going through a high temperature processing. This presents interest for applications. The work deals with laser ablated ZnFe2O4 films deposited at O-2 pressure of 0.16 mbar onto fused quartz substrates. The films about 120 nm thick are nanocrystalline and their spontaneous magnetization, 4 pi Ms, depends on the nanograin size, which is controlled by the substrate temperature (T-s). At T-s approximate to 350 degrees C, where the grain distribution peaks around similar to 20-30 nm, the room temperature 4 pi Ms reaches a maximum of similar to 2.3 kG. The films were studied by magnetooptical polar Kerr effect (MOKE) spectroscopy at photon energies between 1 and 5 eV. The complementary characteristics were provided by spectral ellipsometry (SE). Both the SE and MOKE spectra confirmed ferrimagnetic ordering. The structural details correspond to those observed in MgFe2O4 and Li0.5Fe2.5O4 spinels. SE experiments confirm the insulator behavior. The films display MOKE amplitudes somewhat reduced with respect to those in Li0.5Fe2.5O4 and MgFe2O4 due to a lower degree of spinel inversion and nanocrystalline structure. The results indicate that the films are free of oxygen vacancies and Fe3+-Fe2+ exchange. (C) 2015 AIP Publishing LLC.
 
Publisher AMER INST PHYSICS
 
Date 2016-01-15T07:41:35Z
2016-01-15T07:41:35Z
2015
 
Type Article
 
Identifier JOURNAL OF APPLIED PHYSICS, 117(17)
0021-8979
1089-7550
http://dx.doi.org/10.1063/1.4916936
http://dspace.library.iitb.ac.in/jspui/handle/100/18076
 
Language en