Comparison of Three Design Architectures for Quantum Dot Infrared Photodetectors: InGaAs-Capped Dots, Dots-in-a-Well, and Submonolayer Quantum Dots

DSpace at IIT Bombay

View Archive Info
 
 
Field Value
 
Title Comparison of Three Design Architectures for Quantum Dot Infrared Photodetectors: InGaAs-Capped Dots, Dots-in-a-Well, and Submonolayer Quantum Dots
 
Creator GHADI, H
SENGUPTA, S
SHETTY, S
MANOHAR, A
BALGARKASHI, A
CHAKRABARTI, S
PENDYALA, NB
PRAJAPATI, SL
KUMAR, A
 
Subject TEMPERATURE
THICKNESS
Infrared detectors
photodetectors
photoluminescence
quantum dots
 
Description In this letter, we compare three design architectures for quantum dot infrared photodetectors-InGaAs-capped InAs dots, InAs dot-in-a-well (DWELL), and InAs submonolayer (SML) heterostructures-in terms of optical and spectral behavior. The photoluminescence (PL) intensity measured of the SML sample at 8 K was 20 times stronger than that of the other samples, and its full-width at half-maximum value broader than the rest. Activation energy was calculated using temperature-dependent PL and dark current measurements, which showed the same trend. Peak spectral responses for the InGaAs-capped InAs dot and DWELL samples were observed at 4.1 and 7.3 mu m and at 4.1 and 8.5 mu m, respectively; however, only a single transition was observed for the SML sample because of the absence of a wetting layer. Spectral response of DWELL sample exhibited bias tunability at 87 K, and the SML sample exhibited high temperature of operation till 110 K. One order increment in responsivity was observed in the SML sample compared to others. The peak detectivity of InGaAs-capped InAs dot, DWELL, and SML samples was 4.1 x 10(9), 4.99 x 10(9), and 3.89 x 10(9) Jones, respectively, at 87 K.
 
Publisher IEEE-INST ELECTRICAL ELECTRONICS ENGINEERS INC
 
Date 2016-01-15T09:31:38Z
2016-01-15T09:31:38Z
2015
 
Type Article
 
Identifier IEEE TRANSACTIONS ON NANOTECHNOLOGY, 14(4)603-607
1536-125X
1941-0085
http://dx.doi.org/10.1109/TNANO.2015.2432044
http://dspace.library.iitb.ac.in/jspui/handle/100/18258
 
Language en