Synthesis and characterization of SnS, ZnO nanostructures and SnS/ZnO nanocomposite

Shodhganga@INFLIBNET

View Archive Info
 
 
Field Value
 
Title Synthesis and characterization of SnS, ZnO nanostructures and SnS/ZnO nanocomposite
-
 
Contributor Muthamizhchelvan, C
 
Subject Physics
nanocomposite
 
Description In recent years, research on semiconductor nanostructures and nanocomposite has attracted much attention due to changes in the fundamental properties as a function of size and shape. These nanostructures have been applied in the field of solar cells, detectors, optoelectronic devices, sensors etc. In this work, synthesis, structural and optical properties of SnS, ZnO nanostructures and their nanocomposite were investigated. SnS, ZnO nanostructures and SnS/ZnO nanocomposite were synthesized through chemical route and its structural and optical properties were studied by using X-ray diffraction, transmission electron microscopy, UV-VIS-NIR optical absorption, Raman and photoluminescence spectroscopy. SnS nanoparticles with size varying from 7 to 15 nm were synthesized at room temperature. The direct and indirect band gap transitions were observed at 1.78 eV and 1.2 eV respectively. Compared to bulk SnS, there is an increase in the band gap of SnS nanoparticles due to the quantum confinement effect. The direct band gap transition emission was observed at 1.57 eV from the photoluminescence spectrum of SnS nanoparticles. All the predicted Raman modes were observed and the modes were shifted towards lower wavenumber side. This is due to the phonon confinement effect. SnS nanosheets were formed by the agglomeration of small size SnS nanoparticles (13 nm). The direct band gap transition was observed at 1.88 eV. The band gap emission and defect level emission were observed at 1.75 and 1.57 eV respectively from the photoluminescence spectrum of SnS nanosheets. SnS nanostructures (nanoparticles, nanosheets and nanorods) were synthesized at 180 °C. Shape evolution, from nanoparticle to nanorods was achieved by varying the reaction time. The formation mechanism SnS nanostructures were discussed with respect to reaction time. The UV-VIS-NIR spectrum of SnS nanostructures shows direct and indirect band gap transitions at 1.26 eV and 1.12 eV respectively.
Bibliography p. 120-134, Images given
 
Date 2013-08-07T09:23:47Z
2013-08-07T09:23:47Z
2013-08-07
n.d.
2012
n.d.
 
Type Ph.D.
 
Identifier http://hdl.handle.net/10603/10475
 
Language English
 
Relation -
 
Rights university
 
Format xix,137p.
-
None
 
Coverage Physics
 
Publisher Kattankulathur
SRM University
Department of Physics
 
Source INFLIBNET