Title Jute-fibre glass-plywood/particle board composite
 
Creator Goswami, D N
Ansari, M F
Day, A
Prasad, N
Baboo, B
 
Subject Jute-fibre glass plywood
Particle board composite
Fibre reinforced composite
 
Description 325-331
Jute-fibre glass reinforced sheets were prepared with shellac-containing sheet moulding compound. Highest tensile strength and tensile modulus values of jute-fibre glass composites were obtained in the range of 49.76-51.71 MPa and 1.84–1.85 Gpa repectively. Flexural strength and flexural modulus were found to be 72.97-95.98 Mpa and 2.7-4.2 GPa respectively. Flexural strength values were found to be in the range of those of the reinforced sheets prepared using fiberglass alone, when the thickness of the sheets was increased up to 7-7.5 mm. Flame retardance of the sheets could be improved with the use of flame retardant. Thermal resistance of the sheets was found to be upto 220oC. Lamination of plywood and particleboard was also tried with jute-fibre glass, which yielded improved mechanical properties.
 
Date 2009-01-20T04:45:09Z
2009-01-20T04:45:09Z
2008-07
 
Type Article
 
Identifier 0971–457X
http://hdl.handle.net/123456789/2817
 
Language en_US
 
Publisher CSIR
 
Source IJCT Vol.15(4) [July 2008]