Synthesis and luminescent properties of red-emitting Ba<sub>3-x</sub>Al<sub>2</sub>O<sub>6</sub>:xEu<sup>3+ </sup>phosphor

Online Publishing @ NISCAIR

View Archive Info
 
 
Field Value
 
Authentication Code dc
 
Title Statement Synthesis and luminescent properties of red-emitting Ba<sub>3-x</sub>Al<sub>2</sub>O<sub>6</sub>:xEu<sup>3+ </sup>phosphor
 
Added Entry - Uncontrolled Name Zhao, Ying
 
Uncontrolled Index Term Ba3Al2O6:Eu3+; Phosphors; White light-emitting diode; Luminescence; Photoluminescence
 
Summary, etc. <p>Abstract: Ba<sub>3</sub>Al<sub>2</sub>O<sub>6</sub>:Eu<sup>3+</sup><sup> </sup>phosphor has been prepared by solid state reaction method. X-ray powder diffraction (XRD) analysis confirmed the phase formation of BaAl<sub>2</sub>O<sub>6</sub>:Eu<sup>3+</sup> and the doping of Eu<sup>3+</sup> did not change the crystal structure. The scanning electron microscope (SEM) image exhibited the irregular morphology of Ba<sub>3</sub>Al<sub>2</sub>O<sub>6</sub>:Eu<sup>3+</sup> particles, the particle diameter of the sample is not very uniform, and there is a reunion phenomenon. The photoluminescence excitation (PLE) and emission (PL) spectra were investigated. The fluorescence spectra showed that the fluorescence powder produced by Eu<sup>3+</sup> was the highest when the doping concentration of Eu<sup>3+</sup> was 9 mol%.</p>
 
Publication, Distribution, Etc. Indian Journal of Chemistry -Section A (IJCA)
2020-10-12 16:04:25
 
Electronic Location and Access application/pdf
http://op.niscair.res.in/index.php/IJCA/article/view/22661
 
Data Source Entry Indian Journal of Chemistry -Section A (IJCA); ##issue.vol## 58, ##issue.no## 3 (2019): INDIAN JOURNAL OF CHEMISTRY- SECTION A
 
Language Note en
 
Nonspecific Relationship Entry http://op.niscair.res.in/index.php/IJCA/article/download/22661/465471989
http://op.niscair.res.in/index.php/IJCA/article/download/22661/465471990
 
Terms Governing Use and Reproduction Note Except where otherwise noted, the Articles on this site are licensed under Creative Commons License: CC Attribution-Noncommercial-No Derivative Works 2.5 India© 2015. The Council of Scientific &amp; Industrial Research, New Delhi.