<strong>Effect of alumina impurity on microstructure and properties of alumina based conventionally brazed joints</strong>

Online Publishing @ NISCAIR

View Archive Info
 
 
Field Value
 
Authentication Code dc
 
Title Statement <strong>Effect of alumina impurity on microstructure and properties of alumina based conventionally brazed joints</strong>
 
Added Entry - Uncontrolled Name Dandapat, Nandadulal ; Bio-ceramics and Coating Division, CSIR- Central Glass and Ceramic Research Institute, Kolkata 700 032, India
Ghosh, Sumana ; Bio-ceramics and Coating Division, CSIR- Central Glass and Ceramic Research Institute, Kolkata 700 032, India
Ghosh, Sumana ; Bio-ceramics and Coating Division, CSIR- Central Glass and Ceramic Research Institute, Kolkata 700 032, India
 
Uncontrolled Index Term Alumina ceramics, Impurity effect, Metallization, Brazing, Microstructure, Characterization, Adhesion, Brazing strength
 
Summary, etc. Mo-Mn metallization of alumina ceramics of different purity has been performed at 1400 °C for 10 min in moisthydrogen and nitrogen atmosphere. Nickel coating has been applied onto the metallized alumina ceramics at 1000 °C for 1 hin a reducing hydrogen atmosphere. Finally, metallized and nickel coated alumina ceramics has been brazed with anothermetallized and nickel coated alumina ceramics using CuAg filler alloy at 900 °C for 10 min in a vacuum furnace at 1×10-6Torr pressure. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) analysishas been carried out for phase analysis, microstructural investigation and elemental composition analysis. The adhesivestrength of the metallizing layer and brazing strength of the joint have been measured by pull down breaking strengthmethod. SEM study has shown that the width of the interfacial reaction region between the metallizing layer and substrateenhances with increasing the impurity content in the alumina ceramics. It has been observed that the adhesive strength of themetallizing layer depends on the interfacial reaction layer thickness. The adhesive strength of the metallizing layer has beenincreased with increasing the thickness of interfacial reaction layer. High adhesive strength of the metallizing layer as wellas brazing strength has beenachieved for alumina ceramics with high impurity content.
 
Publication, Distribution, Etc. Indian Journal of Engineering and Materials Sciences (IJEMS)
2021-02-02 15:29:42
 
Electronic Location and Access application/pdf
http://op.niscair.res.in/index.php/IJEMS/article/view/45876
 
Data Source Entry Indian Journal of Engineering and Materials Sciences (IJEMS); ##issue.vol## 27, ##issue.no## 1 (2020): IJEMS- February 2020
 
Language Note en
 
Terms Governing Use and Reproduction Note Except where otherwise noted, the Articles on this site are licensed under Creative Commons License: CC Attribution-Noncommercial-No Derivative Works 2.5 India © 2015. The Council of Scientific &amp; Industrial Research, New Delhi.