Improved Photocatalytic Properties of Bismuth Molybdate Prepared by using High Energy Ball Milling Technique for Degradation of Rhodamine B

NOPR - NISCAIR Online Periodicals Repository

View Archive Info
 
 
Field Value
 
Title Improved Photocatalytic Properties of Bismuth Molybdate Prepared by using High Energy Ball Milling Technique for Degradation of Rhodamine B
 
Creator Khanam, Shomaila
Pradhan, Mangaraj
Rout, Sanjeeb Kumar
 
Subject Photocatalysis
Electron scavengers
Photo-degradation
Rhodamine B
 
Description 398-403
Bismuth molybdate (Bi2MoO6) was prepared through the solid-state route in the stoichiometric ratio followed by ball milling. The high-energy ball milling reduced the crystalline size from 96 to 35nm and increased the surface area from 0.351616 to10.7256 m²/g in 5h. No structural change was observed. The comparative study of the photo catalytic activity for the decolorization of Rhodamine B (RhB) in the presence of UV light has been done by employing 5h milled Bi2MoO6 and unmilled Bi2MoO6 as a catalyst has been done. The dye degradation was observed by a decrease in the absorption spectrum and decolorization in the presence of UV irradiation. The 5h milled Bi2MoO6 proved to be the efficient photocatalyst over unmilled Bi2MoO6. The degradation efficiency of the unmilled and 5h ball milled (Bi2MoO6) catalyst, observed in RhB was found to be 30 and 80% respectively. The degradation efficiency was found to be dependent on the size of the catalyst added in the dye solution may be due to increased surface area provided the increased number of active sites for the reaction. Therefore, 5h ball-milled Bi2MoO6 can act as a catalyst for the treatment of noxious and imperishable organic pollutants in water.
 
Date 2021-06-11T09:34:37Z
2021-06-11T09:34:37Z
2021-05
 
Type Article
 
Identifier 0975-0959 (Online); 0301-1208 (Print)
http://nopr.niscair.res.in/handle/123456789/57466
 
Language en_US
 
Rights CC Attribution-Noncommercial-No Derivative Works 2.5 India
 
Publisher NISCAIR-CSIR, India
 
Source IJPAP Vol.59(05) [May 2021]