<strong>Structural, dielectric and ac electrical properties of nano-structured Mn0.6Co0.2Ni0.2Fe2O4 ternary ferrite synthesized by citrate-gel auto-combustion technique</strong>

Online Publishing @ NISCAIR

View Archive Info
 
 
Field Value
 
Authentication Code dc
 
Title Statement <strong>Structural, dielectric and ac electrical properties of nano-structured Mn0.6Co0.2Ni0.2Fe2O4 ternary ferrite synthesized by citrate-gel auto-combustion technique</strong>
 
Added Entry - Uncontrolled Name Hathiya, Laxmi J; Department of Physics, Saurashtra University
Baraliya, J D
Jethva, H O
Joshi, H H
Not applicable
 
Uncontrolled Index Term Nano ferrite; Auto-combustion; XRD; FTIR; Dielectric; Cole-cole plot
 
Summary, etc. The present paper reports the structural, dielectric and ac electrical properties of nanoparticles of mixed polycrystalline spinel ferrite ternary compound Mn0.6Co0.2Ni0.2Fe2O4 synthesized by using the citrate-gel auto-combustion technique. The standard characterization techniques such as EDAX, XRD and FTIR were primarily employed to confirm the elemental stoichiometry, crystallized single-phase, IR-functional groups. These measurements ascertained the formation of monophasic and pure ferrite compound. The powder X-ray diffraction analysis was done to determine the lattice constant(0.8420 nm), crystallite size(21 nm), X-ray density (5.16 g/cm3), distribution of cations among the tetrahedral and octahedral sites of spinel lattice(with iron-Fe3+ distribution ratio among A and B sites is 0.25), bond angles and bond lengths. The theoretical lattice constant is found to be 0.8422 nm. The nature and position of the IR-bands were observed through FTIR spectroscopy. The high-frequency band v1 (A-site vibrations) lies at 563.07 cm-1 while the low-frequency band v2 (B-site vibrations) lies at 462.59 cm-1 . The force constants for the tetrahedral site (kt) and octahedral site (ko) were deduced 1.33×102 N/m and 1.27× 102 N/m, respectively. Frequency dependence of dielectric constant and tangent loss has been explained by the Maxwell Wagner model and Koop's theory. The Jonscher’s power low was used to describe the ac conductivity measurements. The Nyquist and cole-cole plots indicated presence of grain contribution in the conduction mechanism.
 
Publication, Distribution, Etc. Indian Journal of Pure & Applied Physics (IJPAP)
2022-01-17 13:37:25
 
Electronic Location and Access application/pdf
http://op.niscair.res.in/index.php/IJPAP/article/view/54818
 
Data Source Entry Indian Journal of Pure & Applied Physics (IJPAP); ##issue.vol## 60, ##issue.no## 1 (2022): Indian Journal of Pure & Applied Physics
 
Language Note en
 
Nonspecific Relationship Entry http://op.niscair.res.in/index.php/IJPAP/article/download/54818/465577362
http://op.niscair.res.in/index.php/IJPAP/article/download/54818/465577366
http://op.niscair.res.in/index.php/IJPAP/article/download/54818/465577368
http://op.niscair.res.in/index.php/IJPAP/article/download/54818/465577370
 
Terms Governing Use and Reproduction Note Except where otherwise noted, the Articles on this site are licensed under Creative Commons License: CC Attribution-Noncommercial-No Derivative Works 2.5 India © 2015. The Council of Scientific &amp; Industrial Research, New Delhi.