Hot corrosion performance of bare and coated T91 steel under actual and simulated bio-fuel fired boiler environment<br />

Online Publishing @ NISCAIR

View Archive Info
 
 
Field Value
 
Authentication Code dc
 
Title Statement Hot corrosion performance of bare and coated T91 steel under actual and simulated bio-fuel fired boiler environment<br />
 
Added Entry - Uncontrolled Name Kumar, Manoj ; Department of Mechanical Engineering, Thapar Institute of Engineering and Technology, Patiala, Punjab 1470 01, India
Mudgal, Deepa ; Department of Mechanical Engineering, Thapar Institute of Engineering and Technology, Patiala, Punjab 1470 01, India
Ahuja, Lalit ; Department of Mechanical Engineering, Sant Longowal Institute of Engineering and Technology, Punjab 148 001, India
 
Uncontrolled Index Term materials science
Boiler steel, Hot corrosion, Detonation gun, Coating
 
Summary, etc. The conventional fuel has now been replaced by bio-fuels, due to an increasing demand of power supply which has only been met through the non-renewable resources so far. However, burning of bio-fuel creates corrosive atmosphere which is different from that of coal and oil firing. Therefore, in the present investigation, bare and coated boiler steel T91 substrates were exposed to real andsimulated bio-fuel fired boiler environment working at high temperature. It was noticed that dense and protective oxide was present on Cr3C2-NiCr coated T91 steel after 50hours of exposure in the simulated environment which depicts the protective behaviour of the coating and compatibility of coating with steel despite of variation in the composition. However, oxide so formed in actual bio-fuel fired boiler was porous. WC-Co coated T91 steel has undergone severe corrosion by showing the oxide spallation and delamination of the coating from the substrate under a simulated environment. Similar observations were noticed in the actual boiler working at the temperature of 750±50°C.
 
Publication, Distribution, Etc. Indian Journal of Engineering and Materials Sciences (IJEMS)
2022-07-08 17:18:18
 
Electronic Location and Access application/pdf
http://op.niscair.res.in/index.php/IJEMS/article/view/46113
 
Data Source Entry Indian Journal of Engineering and Materials Sciences (IJEMS); ##issue.vol## 29, ##issue.no## 2 (2022): IJEMS-APRIL 2022
 
Language Note en
 
Terms Governing Use and Reproduction Note Except where otherwise noted, the Articles on this site are licensed under Creative Commons License: CC Attribution-Noncommercial-No Derivative Works 2.5 India © 2015. The Council of Scientific &amp; Industrial Research, New Delhi.