<strong>Studies on characteristics and corrosion behaviour of chitosan/eudragit RS100 bilayer film coated Ti-6Al-4V</strong>

Online Publishing @ NISCAIR

View Archive Info
 
 
Field Value
 
Authentication Code dc
 
Title Statement <strong>Studies on characteristics and corrosion behaviour of chitosan/eudragit RS100 bilayer film coated Ti-6Al-4V</strong>
 
Added Entry - Uncontrolled Name Narayana, Badiadka ; Mangalore University
 
Uncontrolled Index Term  Dental implant; Artificial saliva; Scratch test; Potentiodynamic polarization; Critical load 
 
Summary, etc. <p><span>In the present study, implant material Ti-6Al-4V has been coated with eudragit (EU) and chitosan (CH) polymers to enhance surface properties. The deposition of polymer coating has covered the surface cracks to a significant level and the fact has been confirmed by FE-SEM coupled with EDAX wherein the atomic percentage of Ti (99.90%) in non-coated surface has been decreased markedly to 0.42% after coating. Scratch resistance and adhesion power of bilayer coating has been increased as indicated by the higher critical loads Lc1 (16.71 N), Lc2 (17.56 N), Lc3 (17.96 N) when a progressive load of 1 N to 20 N is applied over the coated surface. Further, Electrochemical impedance spectroscopy (EIS) and potentiodynamic-polarization studies have shown that the value of polarization resistance is inversely proportional to the corrosion rate. Thus decrease in the corrosion rate from 107.5×10-2 (mm year-1) for the non-coated alloy to 2.88×10-2 (mm year-1) for CH/EU coating demonstrated that coating enhanced the corrosion resistance of the alloy in the physiological condition. The in vitro antibacterial test conducted against S. aureus, B. subtilis, P. vulgaris and P. auregenosa has shown a significant inhibition zone of 9 mm, 6 mm, 7 mm and 10 mm, respectively, thus indicating the possible application of the polymeric coating material on the dental implants.</span></p>
 
Publication, Distribution, Etc. Indian Journal of Chemical Technology (IJCT)
2023-07-12 15:11:10
 
Electronic Location and Access application/pdf
http://op.niscair.res.in/index.php/IJCT/article/view/69328
 
Data Source Entry Indian Journal of Chemical Technology (IJCT); ##issue.vol## 30, ##issue.no## 4 (2023): Indian Journal of Chemical Technology
 
Language Note en